Etude du comportement mécanique de structures sandwiches à differents materiaux de revetements / Fairouz Bourouis
![]()
Titre : Etude du comportement mécanique de structures sandwiches à differents materiaux de revetements Type de document : texte imprimé Auteurs : Fairouz Bourouis ; Fay?al Mili, Directeur de thèse ; Univ. de Constantine, Éditeur scientifique Année de publication : 2005 Importance : 106 f. Note générale : 01 Disponible à la salle de recherche 02 Disponibles au magazin de la bibliothèque centrale 01 CD Langues : Français (fre) Catégories : Français - Anglais
Génie MécaniqueTags : Résistance Revêtement Matériau sandwich Ame Flexion cylindrique Flambement Déformations
Sandwich material Coating Heart, Cylindrical bending, buckling,
Resistance, Deformation.Index. décimale : 620 Génie Mécanique Résumé : The sandwich material, present a certain interest in term of rigidity and specific
resistance for the aeronautic structure design. The study of this material meets always
the choice problem of their constituants (coating and heart) in order to load the optimal
mechanical characteristics.
The aim of our work is to do a comparative study of the mechanical behaviour of the
sandwich plates with various materials of coatings charged in cylindrical bending and
compression by taking into account of transverse shearning. For this reason, the
coatings are considered at the base of wood (plywood) or composite laminates ( glass/
epoxy, graphite/epoxy or kevlar /epoxy) of stacking sequence [-
θ
/+
θ
]
5s
and [90
°
/0
°
]
5s
and
the heart is in balsa, aluminium honeycomb, moss herex, or plast honeycomb .The
mechanical behaviour of the sandwich plates was determinated by the use of the
mathematical approaches based on the formulation of the equilibrium equations, and the
development of the classical theory of thin laminated plates .The change of the nature
constituent material as well as the research of the effect of the plate dimensions and the
orientation of fibers reinforcing the composite coatings permit to determine the evolution
of the plates resistance and their deformations, and to calculate the stress in each layer
composing the coatings superior and inferior.
The obtained different results were shaw that the sandwich material with coating in
graphite /epoxy and with heart in aluminium honeycomb resist in buckling and cylindrical
bending better .In return the material at the base of wood (plywood/balsa),is
characterized by a low mechanical resistance. The adequate choice of the coating
material thus ensures a better behaviour of all the sandwich plate.
Diplôme : Magistère En ligne : ../theses/gmecanique/BOU4390.pdf Permalink : index.php?lvl=notice_display&id=881 Etude du comportement mécanique de structures sandwiches à differents materiaux de revetements [texte imprimé] / Fairouz Bourouis ; Fay?al Mili, Directeur de thèse ; Univ. de Constantine, Éditeur scientifique . - 2005 . - 106 f.
01 Disponible à la salle de recherche 02 Disponibles au magazin de la bibliothèque centrale 01 CD
Langues : Français (fre)
Catégories : Français - Anglais
Génie MécaniqueTags : Résistance Revêtement Matériau sandwich Ame Flexion cylindrique Flambement Déformations
Sandwich material Coating Heart, Cylindrical bending, buckling,
Resistance, Deformation.Index. décimale : 620 Génie Mécanique Résumé : The sandwich material, present a certain interest in term of rigidity and specific
resistance for the aeronautic structure design. The study of this material meets always
the choice problem of their constituants (coating and heart) in order to load the optimal
mechanical characteristics.
The aim of our work is to do a comparative study of the mechanical behaviour of the
sandwich plates with various materials of coatings charged in cylindrical bending and
compression by taking into account of transverse shearning. For this reason, the
coatings are considered at the base of wood (plywood) or composite laminates ( glass/
epoxy, graphite/epoxy or kevlar /epoxy) of stacking sequence [-
θ
/+
θ
]
5s
and [90
°
/0
°
]
5s
and
the heart is in balsa, aluminium honeycomb, moss herex, or plast honeycomb .The
mechanical behaviour of the sandwich plates was determinated by the use of the
mathematical approaches based on the formulation of the equilibrium equations, and the
development of the classical theory of thin laminated plates .The change of the nature
constituent material as well as the research of the effect of the plate dimensions and the
orientation of fibers reinforcing the composite coatings permit to determine the evolution
of the plates resistance and their deformations, and to calculate the stress in each layer
composing the coatings superior and inferior.
The obtained different results were shaw that the sandwich material with coating in
graphite /epoxy and with heart in aluminium honeycomb resist in buckling and cylindrical
bending better .In return the material at the base of wood (plywood/balsa),is
characterized by a low mechanical resistance. The adequate choice of the coating
material thus ensures a better behaviour of all the sandwich plate.
Diplôme : Magistère En ligne : ../theses/gmecanique/BOU4390.pdf Permalink : index.php?lvl=notice_display&id=881 Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité BOU/4390 BOU/4390 Thèse Bibliothèque principale Thèses Disponible
Titre : Etude du phénomène d'usure sous sollicitations complexes des vis d'extrusion : perspéctive de revêtement Type de document : texte imprimé Auteurs : Ali Kherbouche ; Christian Coddet, Directeur de thèse ; Université de technologie de Compiegne, Éditeur scientifique Année de publication : 1987 Importance : 62 f. Note générale : Disponible à la salle de recherche Langues : Français (fre) Catégories : Français - Anglais
Génie MécaniqueTags : Usure Extrusion Revêtement Index. décimale : 620 Génie Mécanique Permalink : index.php?lvl=notice_display&id=798 Etude du phénomène d'usure sous sollicitations complexes des vis d'extrusion : perspéctive de revêtement [texte imprimé] / Ali Kherbouche ; Christian Coddet, Directeur de thèse ; Université de technologie de Compiegne, Éditeur scientifique . - 1987 . - 62 f.
Disponible à la salle de recherche
Langues : Français (fre)
Catégories : Français - Anglais
Génie MécaniqueTags : Usure Extrusion Revêtement Index. décimale : 620 Génie Mécanique Permalink : index.php?lvl=notice_display&id=798 Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité KHE/1665 KHE/1665 Thèse Bibliothèque principale Thèses Disponible Caractérisation de la réaction interfaciale entre une couche mince de tungsèe et un substrat d'acier / Mourad Khechba
![]()
Titre : Caractérisation de la réaction interfaciale entre une couche mince de tungsèe et un substrat d'acier Type de document : texte imprimé Auteurs : Mourad Khechba ; Univ. de Constantine, Éditeur scientifique ; Rachid Halimi, Directeur de thèse Année de publication : 2008 Importance : 82 f. Note générale : 01 Disponible à la salle de recherche 02 Disponibles au magazin de la B.U.C. 01 CD Langues : Français (fre) Catégories : Français - Anglais
PhysiqueTags : Thin films magnetron sputtering coating tungsten carbides Couches Minces pulvérisation cathodique RF revêtement tungstène carbures Index. décimale : 530 Physique Résumé : In this work, we characterize the reaction of tungsten thin layer (6µm thickness) deposited by rf magnetron sputtering technique at 500°C, during 60min, with a steel XC70 substrate (according to AFNOR) containing 0,7 % of carbon.
The samples (thin layer of tungsten + steel substrate) were submitted to thermal treatments in vacuum at various temperatures (500°C-1000°C) and during different times. The specimens are characterized by X ray diffraction (XRD), optic microscopy, scanning electron microscopy (SEM) and by Vickers tests for the measurements of micro-hardness.
The main obtained results can be summarized as follows:
In the temperature range 500-800°C, no formation of tungsten carbides was observed. However, the annealing at a temperature greater than or equal to 900°C promotes the reaction between the constituents of the samples (W, Fe, C), and hence the formation of W2C carbide. No other compounds were detected.
The micro-hardness measured by Vickers tests, increases with the rise in temperature, particularly from 900°C. The increase in the hardness is due, probably, to the formation and growth of W2C carbide.
It is also shown that, the micro-hardness decreases with increasing of the applied load and the depth of penetration until substrate.
For thin coating (2 and 4 μm):
W2C carbide is formed with annealing at 800 ° C for 30 min for all samples.
The formation of ternary carbide Fe3W3C takes place after annealing at T≥ 900°C.
The mono carbide WC is obtained with an annealing at 1000°C for 60 min, only in
the case of the thinner coating (2 μm).
The morphology of the surface samples depends on the temperature and duration of thermal annealing.Diplôme : Magistère En ligne : ../theses/physique/KHE5087.pdf Permalink : index.php?lvl=notice_display&id=3468 Caractérisation de la réaction interfaciale entre une couche mince de tungsèe et un substrat d'acier [texte imprimé] / Mourad Khechba ; Univ. de Constantine, Éditeur scientifique ; Rachid Halimi, Directeur de thèse . - 2008 . - 82 f.
01 Disponible à la salle de recherche 02 Disponibles au magazin de la B.U.C. 01 CD
Langues : Français (fre)
Catégories : Français - Anglais
PhysiqueTags : Thin films magnetron sputtering coating tungsten carbides Couches Minces pulvérisation cathodique RF revêtement tungstène carbures Index. décimale : 530 Physique Résumé : In this work, we characterize the reaction of tungsten thin layer (6µm thickness) deposited by rf magnetron sputtering technique at 500°C, during 60min, with a steel XC70 substrate (according to AFNOR) containing 0,7 % of carbon.
The samples (thin layer of tungsten + steel substrate) were submitted to thermal treatments in vacuum at various temperatures (500°C-1000°C) and during different times. The specimens are characterized by X ray diffraction (XRD), optic microscopy, scanning electron microscopy (SEM) and by Vickers tests for the measurements of micro-hardness.
The main obtained results can be summarized as follows:
In the temperature range 500-800°C, no formation of tungsten carbides was observed. However, the annealing at a temperature greater than or equal to 900°C promotes the reaction between the constituents of the samples (W, Fe, C), and hence the formation of W2C carbide. No other compounds were detected.
The micro-hardness measured by Vickers tests, increases with the rise in temperature, particularly from 900°C. The increase in the hardness is due, probably, to the formation and growth of W2C carbide.
It is also shown that, the micro-hardness decreases with increasing of the applied load and the depth of penetration until substrate.
For thin coating (2 and 4 μm):
W2C carbide is formed with annealing at 800 ° C for 30 min for all samples.
The formation of ternary carbide Fe3W3C takes place after annealing at T≥ 900°C.
The mono carbide WC is obtained with an annealing at 1000°C for 60 min, only in
the case of the thinner coating (2 μm).
The morphology of the surface samples depends on the temperature and duration of thermal annealing.Diplôme : Magistère En ligne : ../theses/physique/KHE5087.pdf Permalink : index.php?lvl=notice_display&id=3468 Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité KHE/5087 KHE/5087 Thèse Bibliothèque principale Thèses Disponible Etude de l’influence de l’azote et du recuit thermique sur les propriétés de films minces de nitrure de chrome / Halima Lehbili
![]()
Titre : Etude de l’influence de l’azote et du recuit thermique sur les propriétés de films minces de nitrure de chrome Type de document : texte imprimé Auteurs : Halima Lehbili, Auteur ; A. Bouabellou, Directeur de thèse Editeur : Constantine : Université Mentouri Constantine Année de publication : 2010 Importance : 123 f. Format : 31 cm. Note générale : Magister
2 copies imprimées disponiblesLangues : Français (fre) Catégories : Français - Anglais
PhysiqueTags : Couche Mince chrome revêtement pulvérisation cathodique RF carbures nitrures carbonitrure nanoindentation Index. décimale : 530 Physique En ligne : ../theses/physique/LEH6064.pdf Format de la ressource électronique : Permalink : index.php?lvl=notice_display&id=5976 Etude de l’influence de l’azote et du recuit thermique sur les propriétés de films minces de nitrure de chrome [texte imprimé] / Halima Lehbili, Auteur ; A. Bouabellou, Directeur de thèse . - Constantine : Université Mentouri Constantine, 2010 . - 123 f. ; 31 cm.
Magister
2 copies imprimées disponibles
Langues : Français (fre)
Catégories : Français - Anglais
PhysiqueTags : Couche Mince chrome revêtement pulvérisation cathodique RF carbures nitrures carbonitrure nanoindentation Index. décimale : 530 Physique En ligne : ../theses/physique/LEH6064.pdf Format de la ressource électronique : Permalink : index.php?lvl=notice_display&id=5976 Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité LEH/6064 LEH/6064 Thèse Bibliothèque principale Thèses Disponible
Titre : Influence des traitements de surface sur les propriétés mécaniques Type de document : texte imprimé Auteurs : Abdeldjalil Djeriba ; Univ. de Constantine, Éditeur scientifique ; E. Ferkous, Directeur de thèse Année de publication : 2007 Importance : 159 f. Note générale : 01 Disponible à la salle de recherche 02 Disponibles au magazin de la B.U.C. 01 CD Langues : Français (fre) Catégories : Français - Anglais
Génie MécaniqueTags : Usure Revêtement Trempe Pulvérisation Plasma Index. décimale : 620 Génie Mécanique En ligne : ../theses/gmecanique/DJE4829.pdf Permalink : index.php?lvl=notice_display&id=682 Influence des traitements de surface sur les propriétés mécaniques [texte imprimé] / Abdeldjalil Djeriba ; Univ. de Constantine, Éditeur scientifique ; E. Ferkous, Directeur de thèse . - 2007 . - 159 f.
01 Disponible à la salle de recherche 02 Disponibles au magazin de la B.U.C. 01 CD
Langues : Français (fre)
Catégories : Français - Anglais
Génie MécaniqueTags : Usure Revêtement Trempe Pulvérisation Plasma Index. décimale : 620 Génie Mécanique En ligne : ../theses/gmecanique/DJE4829.pdf Permalink : index.php?lvl=notice_display&id=682 Exemplaires (1)
Code-barres Cote Support Localisation Section Disponibilité DJE/4829 DJE/4829 Thèse Bibliothèque principale Thèses Disponible